It is widely acknowledged that early detection of material damage and timely rehabilitation can lead to a significant reduction in the life-cycle cost of asphalt pavements. This research investigates the capabilities of damage detection and healing of graphite nanoplatelet (GNP)-taconite modified asphalt materials. The first part of the research is concerned with the application of GNP-taconite modified asphalt materials for damage detection using electrical conductivity. It is shown that, as compared to conventional asphalt materials, the GNP-taconite modified asphalt materials exhibit an improved electrical conductivity due to the electron hopping mechanism. Based on the mathematical analogy between the elastostatic field and the electrostatic field, a theoretical model is derived to relate the change of electrical conductivity to the damage extent of the material. Although, in principle, the material damage can be accessed using the electrical conductivity, the practical application of this method is complicated by the fact that the conductivity is influenced by the moisture content. The second part of the research investigates the damage healing capability of GNP-taconite modified asphalt materials heated by microwave. GNP-taconite modified asphalt materials can effectively absorb the heat generated by the microwave, and the rising temperature can effectively heal the microcracks in the binder. This damage-healing mechanism is verified by a set of semi-circular beam tests. Finally, microwave heating technology is applied to the tack coat system. It is shown that, with microwave heating, the GNP-taconite modified asphalt material can effectively improve the bond strength of the interface of the tack coat system.
Le, Jia-Liang; Marasteanu, Mihai; Zanko, Lawrence; Matias de Oliveira, Jhenyffer; Calhoon, Thomas; Turos, Mugurel; Stricherz, Tyler; Hopstock, David; Hegg, Vern.
Innovative Materials and Advanced Technologies for a Sustainable Pavement Infrastructure.
Minnesota Department of Transportation.
Retrieved from the University of Minnesota Digital Conservancy,
Content distributed via the University of Minnesota's Digital Conservancy may be subject to additional license and use restrictions applied by the depositor.